TS-106A Hardcover kitchen and toilet (blue sky) waterproof coating, composed of high performance polymer emulsion and a variety of inorganic materials, made of two component waterproofing slurry. It can cover tiny cracks and resist slight vibration.
Product characteristics
It can be constructed on wet, complex and rough foundation.
After dry consolidation, tiles can be directly pasted or plastered to leveling.
Non-toxic and harmless, it can be directly used in drinking water ponds and fish ponds.
The coating can inhibit the growth of mould and prevent the pollution of moisture and salt on the decorative surface.
Scope of application
Applicable to home kitchen, bathroom, shower, wardrobe, decorative wall, background wall, ceiling base, moisture-proof base, etc.
Usage method
1. Base treatment: The base should have a solid surface structure with porous, rough, crackless, clear water and no empty drum, and the uneven base should be leveled first.
2. Preparation: first, the B component (emulsion) is poured into a clean container, then the A component (powder) is poured into the emulsion, and the electric mixer is used to stir until uniform without caking. Let the slurry rest for 2 to 4 minutes before stirring again.
3. Construction: Brush or spatula is used to coat at least two layers by cross-over method. The first layer is coated with thick coating so that there is no void at all on the base surface. When the first coat has solidified and produced enough strength, about 2 to 4 hours later, the next coat can be constructed. The total coating thickness should be at least 1.0 mm or more. If necessary, the third floor construction can be carried out.
be
sPerformance parameter
Reference Dosage:1.5-2.0kgs/㎡
Initial setting time: ≥45min
Final setting time: ≤24hours
Construction temperature: +5℃~+35℃
Packaging: 5kgs/set 17.2kgs/set
Implementation standard: JC/T 984-2011(II), specific indicators see technical parameters.
No | Project | Technical standard(II) | ||
1 | Setting time | Initial setting time/min ≥ | 45 | |
Final setting time/h ≤ | 24 | |||
2 | Impermeability pressure/Mpa | Coated specimen≥ | 7d | 0.5 |
Mortar specimen ≥ | 7d | 1 | ||
28d | 1.5 | |||
3 | Compressive strength/Mpa ≥ | 24 | ||
4 | Flexural strength/Mpa ≥ | 8 | ||
5 | Flexibility (transverse deformation capacity)/mm ≥ | 1 | ||
6 | Bond strength/Mpa ≥ | 7d | 1 | |
28d | 1.2 | |||
7 | Alkali resistance | No cracking, peeling | ||
8 | Heat resistance | No cracking, peeling | ||
9 | Frost resistance | No cracking, peeling | ||
10 | Shrinkage rate/% ≤ | 0.15 | ||
11 | Water absorption rate/% ≤ | 4 | ||
Transportation & storage
This product is non-flammable and explosive material, which can be transported according to general cargo. Sunscreen, freeze-proof, rain-proof, extrusion and collision should be avoided in transportation, and the packaging should be kept intact.
The product should be ventilated, dried and prevented from direct sunshine during storage. The storage temperature should be between 5 and 35℃.
Under normal storage and transportation conditions, the storage period is 12 months from the date of production.
Attention
After the waterproof layer is completely dry, the overburden construction can be carried out.
This material should be constructed in the environment of +5 - +35℃, and it is not suitable to be constructed outdoors in rainy weather.
It is strictly forbidden to mix the dried slurry with water for reuse.
This product is alkaline, if splashed into eyes will be irritating, should be washed with clear water in time.