TS-109 JS polymer waterproof coating is made of special polymer waterproof latex as main raw material and various additives. After mixing with cement, the latex can be applied on the base surface to form a flexible waterproof layer with certain elasticity, strong cohesion, impermeability, crack resistance, weatherability, acid and alkali resistance.
Product characteristics
It is easy to operate, easy to construct, and has remarkable impermeability and waterproof effect.
It can be directly constructed on dry exterior wall and wet base surface with strong bonding force.
The product has stable performance, anti-ultraviolet, anti-aging and good weather resistance.
Scope of application
Seepage and moisture-proof treatment of the sky, pool, exterior wall, toilet and bathroom of the building, and basement; seepage and moisture-proof engineering of porous masonry materials such as aerated concrete, hollow brick, etc.
Usage method
1. Base treatment: The base should have a solid surface structure with porous, rough, crackless, clear water and no empty drum, and the uneven base should be leveled first.
2. Preparation: liquid: powder (cement) = 1:0.8 (weight ratio). First pour (emulsion) into a clean container, then pour the cement slowly into the emulsion, and use electric mixer to stir until no agglomeration occurs. Let the slurry be stirred for 2 to 4 minutes.
3. Construction: Brush or spatula is used to coat at least two layers by cross-over method. The first layer is coated with thick coating so that there is no void at all on the base surface. When the first coat has solidified and produced enough strength, about 2 to 4 hours later, the next coat will be constructed. The total coating thickness should be at least 1.0 mm or more. If necessary, the third floor construction can be carried out.
Performance parameter
Reference Dosage:1.5-2.0kgs/㎡
Initial setting time: ≥2hours
Final setting time: ≤48hours
Construction temperature: +5℃~+35℃
Packaging: 5kgs/bucket, 20kgs/bucket
Implementation standard: GB/T23445-2009(II), specific indicators see technical parameters.
No | Project | Technical standard(II) |
1 | Tensile strength/Mpa ≥ | 1.8 |
2 | Fracture elongation /% ≥ | 80 |
3 | Low temperature flexibility | -- |
4 | Bond strength of wet base/Mpa ≥ | 0.7 |
5 | Water impermeability | 0.3Mpa, 30min Impervious |
6 | Solid content /% ≥ | 70 |
7 | Impermeability (backwater surface of mortar) ≥ | 0.6 |
Transportation & storage
This product is non-flammable and explosive material, which can be transported according to general cargo. Sunscreen, freeze-proof, rain-proof, extrusion and collision should be avoided in transportation, and the packaging should be kept intact.
The product should be ventilated, dried and prevented from direct sunshine during storage. The storage temperature should be between 5 and 35℃.
Under normal storage and transportation conditions, the storage period is 12 months from the date of production.
Attention
After the waterproof layer is completely dry, the overburden construction can be carried out.
This material should be constructed in the environment of +5 - +35℃, and it is not suitable to be constructed outdoors in rainy weather.
This product is alkaline, if splashed into eyes will be irritating, should be washed with clear water in time.